Tool Steel A10

Aging Procedure

Not applicable to this alloy.

Annealing Procedure

Anneal at 1425 F and very slow furnace cool at a rate of 25 F per hour or less.

Applications

Typically used for thread rolling dies and other intricate die shapes.

Cold Workability

The alloy may be cold worked in the annealed condition by conventional methods.

Forgeability

The forging temperature range is rather narrow of A10. Forge at 1875 F down to 1650 F. Do not forge below 1600 F.

Formability

Forming is done by means of machining or hot forging.

Hardening Procedure

This alloy hardens by heat treatment. See "Heat Treatment" and "Tempering".

Heat Treatability

Preheat slowly to 1200 F then raise the temperature to 1475 F and hold for 45 to 60 minutes. Remove and air cool (the alloy is air hardening as the quench medium).

Hot Workability

Other than forging it is not usual practice to hot work this alloy. Consult the alloy supplier regarding hot working.

Machinability

As with all of the tool steel alloys the machinability of A10 is medium, similar to the low alloy steels. It has a machinability rating of about 85% that of the simple alloy water hardening tool steels (W group) which are rated at 100% for reference.

Other Comments

A10 alloy has high wear resistance and medium toughness.

Principle Design Features

This alloy is one of the Cold Work, Medium Air Hardening type tool steels. It contains chromium, molybdenum, vanadium and manganese to promote deep hardening without quenching. This keeps distortion at a minimum upon hardening.

Tempering Procedure

Temper at 400 F to 800 F. This will result in developing a hardness of approximately Rockwell C 62 for the low temperature to Rockwell C 55 for the 800 F temper.

Weldability

A10 is an alloy steel and thus capable of being welded. Consult the alloy supplier for details.