Tool Steel M52

Annealing Procedure

Heat to 1550 F and furnace cool slowly. M52 is extremely susceptible to decarburization and must be protected during any thermal treatment.

Applications

Most often employed in tooling applications where abrasion resistance is less important, such as woodworking tools and commercial twist drills.

Forgeability

Preheat to 1500 F and soak thoroughly. Then increase temperature to 2000 F prior to working. Do not forge below 1800 F.

Formability

Not applicable

Hardening Procedure

For optimum performance and stability, preheat work to 1600 F until soaked, then superheat to 2150 F only long enough for the work to reach furnace temperature and quench immediately in oil.

Heat Treatability

See annealing, tempering and hardening.

Machinability

This alloy is best machined in the annealed condition. It is rated at 65 % of a 1% carbon steel, or 50% of a B1112.

Principle Design Features

This alloy is an intermediate high speed, molybdenum - chromium - vanadium type tool steel.

Tempering Procedure

Tempering should immediately follow quenching. For best performance, double temper at 1025 F.